Low temperature growth and properties of ZnO nanorod arrays

Xiang Wu, Huibo Chen, Lihong Gong, Fengyu Qu and Yufeng Zheng

Abstract

In this paper, well aligned ZnO nanorod arrays were synthesized by a simple hydrothermal route at a low temperature. The diameters of the as-synthesized products were 20–60 nm and the lengths were as much as several micrometers. The surfaces and tops of the nanorods were smooth. The as-grown nanorod arrays were investigated by x-ray powder diffraction (XRD), scanning electron microscope (SEM), transmission electron microscope (TEM), photoluminescence (PL) spectroscopy and contact angle (CA) analysis. The as-grown nanorods were single crystalline structures with a wurtzite phase, and grew along the [0001] direction. The PL spectrum with only one strong peak at 383 nm shows good intrinsic emission