pH sensitivity of emeraldine salt polyaniline and poly(vinyl butyral) blend
Hoa Duyen Nguyen, Thi Ha Nguyen, Ngoc Vu Hoang, Nguyen Ngan Le, Thi Ngoc Nhien Nguyen, Duc Chanh Tin Doan and Mau Chien Dang
Abstract
pH sensitivity of emeraldine salt polyaniline (ES-PANI) and poly(vinyl butyral) (PVB) blend film was investigated. This blend film can be used as a pH sensing element in new-type pH sensors to replace traditional instruments based on fragile glass electrodes for pH measurement of water in aquaculture farming. Structural and optical characteristic of PANI were studied by Fourier transform infrared spectroscopy (FTIR) and ultraviolet visible spectroscopy (UV–vis). Electrical characterization of ES-PANI:PVB blend films versus pH was performed with chemiresistors fabricated by micro-lithography. A ES-PANI:PVB layer was drop-coated on comb-shaped platinum electrodes patterned on SiO2/Si substrates. Scanning electron microscope (SEM) and optical microscope were used to investigate morphology of the fabricated platinum electrodes and the coated polymer blend films. I–V measurements of the polymer-coated chemiresistors were performed at very low relative humidity after the polymer films were exposed to pH 1–8. The results showed that logarithm of electrical resistance of the ES-PANI:PVB films increased almost linearly as pH increased from 1 to 8. The initial results showed that the PANI blend-coated chemiresistors can be used as pH sensors for water quality monitoring